Abstract Poultry litter waste (PLW) is the main by-product generated by the Brazilian poultry industry. A sustainable approach for reusing this waste is the production of biochar to be further used aiming CO2 adsorption. In this work, biochars were produced by varying the N2 flow along the pyrolysis process of 150 (PLW-150) and 1000 (PLW-1000) mL min-1. PLW and biochars were characterized for their morphology, porosity, specific surface area, and CO2 adsorption capacity. From the biochars, carbon cryogels (CC) were produced aiming their use as CO2 adsorbents. The results of the cryogel adsorption test showed a CO2 adsorption capacity of 13.1±2.9 and 33.8±3.3 mg g-1 for the CC-PLW.150 and CC-PLW.1000 cryogels, respectively. Therefore, reusing this residue for cryogels production and its use in the CO2 adsorption signifies an attractive perspective to minimize the environmental damage caused by CO2 emissions.

The production of a material with rigid, multifunctional three-dimensional porous structure at a low cost is still challenging to date. In this work, a light and rigid carbon foam was prepared using rice husk as the basic element through a simple fermentation process followed by carbonization. For the fermentation process, the amount of biological yeast (7.5 g for the carbon foam CA-1P and 5 g for the carbon foam CA-2P) was used to evaluate its influence on the morphology of the foams. In order to prove that the heat treatment made in the foam alters the hydrophilic character of the rice husk foam, a chemical treatment with steam deposition was carried out. The foams were characterized by the following analyzes: apparent density, micrograph, thermogravimetry, contact angle, water sorption capacity and thermal conductivity. Visually, the CA-1P foams presented a structure with larger pores due to the greater amount of yeast used in its formulation. The heat treatment of rice potato foams proved to be as efficient as the chemical treatment for water contact angle above 90º, proving the ability of the foams to repel water/moisture. The thermal conductivity of the foams (0.029 and 0.026 W m-1 K-1 for CA-1P and CA-2P, respectively) was close to the conductivity of polyurethane foams (0.032 W m-1 K-1). Thus, the method used in the production of the carbon foams produced from the rice husk proved to be effective. In addition, the foams produced have the potential to be used for thermal insulation.